Model No: 1.6511/4340/40CrNiMoA
UT 1.6511/4340/40CrNiMoA
Application
It is generally used for making important parts with high strength and good plasticity, and for making important parts with special performance requirements after nitrogen treatment, such as shafts, gears and fasteners
It is generally used for making important parts with high strength and good plasticity, and for making important parts with special performance requirements after nitrogen treatment, such as shafts, gears and fasteners
minimum order :
10 tonnes
Quantity :
Subscribe to our Newsletter
UT 1.6511/4340/40CrNiMoA alloy structural steel has high strength, toughness and good hardenability, and anti-overheating stability, but the sensitivity of white spots is high and there is temper brittleness.
Chemical Composition(%)
Application
UT 1.6511/4340/40CrNiMoA alloy structural steel is generally used for making important parts with high strength and good plasticity, and for making important parts with special performance requirements after nitrogen treatment, such as shafts, gears, and fasteners
| Steel Grade | 1.6511/4340/40CrNiMoA |
| Dimension | Thick 10-1500mm x Width 200-3000mm / Diameter Ø8~3000mm |
| Delivery Condition | HB≤229 |
| Surface Treatment | Black Surface / Milled Surface |
| Production Condition | Two Sides Cut or Four Sides Cut |
| Stock Quantity | 1500 tons |
| Ultrasonic Test | Sep1921-84 D/D or E/e Under 100% Test |
| MOQ | 10 tonnes |
| Mill Sheet Certificate | Provided |
| HS Code | Hot Rolled:722830 Forged: 722840 |
| Technique | Hot Rolled / Forged |
| Lead Time | 7-10 days |
| Trademark | UTSTEEL |
Chemical Composition(%)
| C | Si | Mn | Cr | Mo | Ni | S |
| 0.32~0.40 | ≤0.40 | 0.5~0.8 | 0.90~1.20 | 0.15~0.30 | 0.9~1.2 |
Application
UT 1.6511/4340/40CrNiMoA alloy structural steel is generally used for making important parts with high strength and good plasticity, and for making important parts with special performance requirements after nitrogen treatment, such as shafts, gears, and fasteners